31· Effect of process control agent on the structural and magnetic properties of nano/amorphous Fe 0.7 Nb 0.1 Zr 0.1 Ti 0.1 powders prepared by high energy ball milling. …
2019328· A process control agent (PCA), which can be a solid, liquid or gas, is essential in MA to prevent excessive cold welding during ball milling, to prevent the powder from adhering …
Appropriate addition of process control agent (PCA) can reduce the adhesion of the material on the wall and ball surface by in situ surface modification.
920· This study was conducted to investigate the characteristics of the AlCrCuFeNi high-entropy alloy (HEA) synthesized through mechanical alloying (MA). In addition, effects of …
2017925· Surfactant additives are often used in ball milling as process control agents [4, 25,31]. The use of corrosion inhibitors as additives to milling medium is quite relevant because …
201041· The MA process was performed in a planetary ball mill (Retsch, PM400) using zirconia containers and steel balls at room temperature. The weight ratio of ball to powder was …
Nano-silicon powder was prepared by mechanical ball milling using deionized water, n-hexane and absolute ethanol as process control agents. The effects of polar solvent and non-polar …
111· Despite widespread use of liquid process control agents (PCA) during material processing via high-energy ball milling, their effect on the …
215· In this study, using iron stearate as process control agent in the ball milling process suppressed grain growth and produced second-phase nanoinclusions in bulk …
200311· Request PDF | An investigation of the use of stearic acid as a process control agent in high energy ball milling of Nb-Al and Ni-Al powder mixtures | High energy ball milling …
1115· The effect of ethanol as a process control agent (PCA) on the mechanical alloying (MA) of Fe-20 at. % Al powders is presented. MA was performed at room temperature …
215· In this study, using iron stearate as process control agent in the ball milling process suppressed grain growth and produced second-phase nanoinclusions in bulk …
Mechanical alloying is akin to metal powder processing, where metals may be mixed to produce superalloys.Mechanical alloying occurs in three steps. First, the alloy materials are combined …
91· Key MA processing variables that determine the final microstructural evolution in alloy particles are the milling -speed, −time, −temperature, − atmosphere, process control …
The MA process carries out in a Noah-Nuoya® NQM 0.2 L planetary ball mill with parameters according to Table 3. The capacity was 200 g together with the milling spheres, and argon gas …
31· Effect of process control agent on the structural and magnetic properties of nano/amorphous Fe 0.7 Nb 0.1 Zr 0.1 Ti 0.1 powders prepared by high energy ball milling. …
424· It is possible to avoid problems such as the decrease in toughness and ductility caused by ceramic reinforcements in ceramic reinforced metal matrix composites by using …
Container of ball mill 10. Process control agent (PCA). 1.3.1 Ball Mill Type . Ball mills exist in a variety of sizes, capacities, and speeds, and they can control the process by adjusting the …
200311· Request PDF | An investigation of the use of stearic acid as a process control agent in high energy ball milling of Nb-Al and Ni-Al powder mixtures | High energy ball milling …
20191015· High-energy ball milling process can well control the microstructure and morphology of microscale zero-valent aluminum (mZVAl) particles, in which the main …
Container of ball mill 10. Process control agent (PCA). 1.3.1 Ball Mill Type . Ball mills exist in a variety of sizes, capacities, and speeds, and they can control the process by adjusting the …
201781· In this study, the effects of the process control agent (toluene) usage on the product size, morphology and conversion level of precursor powders to MgB 2 after …
2013101· In this study, nanocrystalline Fe-45 wt% Ni alloy powders were prepared by mechanical alloying via high-energy ball milling.The effect of adding stearic acid as a process …
201041· The MA process was performed in a planetary ball mill (Retsch, PM400) using zirconia containers and steel balls at room temperature. The weight ratio of ball to powder was …
819· Fe–Si–B–P–Cu nanocrystalline alloy were treated with ball-mill using a lubricant as a process control agent (PCA). The resulting alloy powder is a strong candidate material for …
201781· In this study, the effects of the process control agent (toluene) usage on the product size, morphology and conversion level of precursor powders to MgB 2 after …